Estudio microtomográfico de la porosidad en la cementación de postes de fibra

Estudio microtomográfico de la porosidad en la cementación de postes de fibra

Microtomographic study of the porosity in the cementation of fiber posts

Trigo Humaran, M. M.

García Cuerva, M.

Cabirta, M. L.

Lenarduzzi, A.

Gualtieri, A.

González Zanotto, C.

Resumen: El objetivo de este estudio fue evaluar con microtomografía los poros existentes entre el cemento de resina, poste de fibra y paredes del conducto en los distintos tercios radiculares en premolares inferiores. Se utilizaron 15 premolares inferiores unirradiculares humanos recientemente extraídos. Se les realizó el tratamiento endodóntico, y se obturó con conos de gutapercha y cemento endodóntico a base de resina. Una vez desobturados se procedió a la cementación de los postes. Cada muestra se posicionó en un accesorio personalizado y se escaneó utilizando un Microtomógrafo. Con el software CTAn v.1.12 (Bruker-microCT) se analizaron las microtomografías para obtener el volumen de interés (VOI) que permitió calcular el área de superficie (mm2) y volumen de cada poro (mm3) entre la dentina y el poste a nivel coronal, medio y apical. Los datos fueron analizados mediante las pruebas estadísticas de Friedman o ANOVA de medidas repetidas. El volumen de los poros entre los tres tercios radiculares mediante la prueba de Friedman, encontró una diferencia global significativa (F = 30,00; p < 0,05). El tercio en donde los poros presentaron un mayor volumen (mm3) fue el tercio coronal (mediana: 0,29250), seguido por los tercios medio (mediana: 0,03200), y apical (mediana: 0,00140). La comparación de la superficie de los poros entre los 3 tercios brindó un resultado análogo al de la comparación del volumen. La mayor superficie (mm2) correspondió al tercio coronal (media ± DE = 1,66377 ± 0,27175), seguido por los tercios medio (media ± DE = 1,16210 ± 0,20343) y apical (media ± DE = 0,41074 ± 0,12641). La microtomografía permitió realizar un análisis cuantitativo y cualitativo de los poros en toda la muestra, sin deterioro de la misma. Se puede concluir que el tercio coronal presenta más poros que el tercio apical con la técnica de cementación utilizada. En cuanto a la superficie y volumen de los poros, los resultados encontrados son similares a los reportados por diversos autores.

Abstract: The aim of this study was to evaluate with microtomography the existing pores between the resin cement, fiber post and canal walls in the different in thirds of the canal, in single-root lower premolars. Fifteen recently extracted human single root lower premolars were used, endodontically treated, and filled with gutta-percha cones and resin-based endodontic cement. Once unfilled, the posts were cemented. Each sample was positioned on a custom fixture and scanned using a Microtomograph. Each sample was evaluated using CTAn v.1.12 software (Bruker-microCT) to obtain the surface area (mm2), volume of interest (mm3) of each pore between dentin and post at the coronal, middle and apical levels. Data were analyzed using Friedman’s tests or repeated measures ANOVA. The volume of the pores between the three root thirds using the Friedman test, a significant global difference was found (F = 30.00; p < 0.05). The third in which the pores presented a greater volume (mm3) was the coronal third (means: 0.29250), followed by the middle (means: 0.03200) and apical (means: 0.00140) thirds. The comparison of the pore surface between the 3 thirds gave an analogous result to that of the volume comparison. The largest surface area (mm2) corresponded to the coronal third (mean ± SD 1.66377 ± 0.27175), followed by the middle (mean ± 1.16210 ± 0.20343) and apical (mean ± 0.41074 ± 0.12641) thirds.Microtomography allowed a quantitative and qualitative analysis of the pores in the entire sample without deterioration. It can be concluded that the coronal third has more pores than the apical third with the cementation technique used. Regarding the surface and volume of the pores, the results found are similar to those reported by various authors.

Fil: Trigo Humaran, M. M. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: García Cuerva, M. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Cabirta, M. L. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Endodoncia. Buenos Aires, Argentina.

Fil: Lenarduzzi, A. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Endodoncia. Buenos Aires, Argentina.

Fil: Gualtieri, A. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Biofísica y Bioestadística. Buenos Aires, Argentina.

Fil: González Zanotto, C. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Rev Fac Odontol, Univ Buenos Aires. 2022; 37(86), 25–36.

ISSN 1668-8538

Universidad de Buenos Aires. Facultad de Odontología.

2022

12 pp.