Resistencia adhesiva de postes de fibra a los diferentes tercios del conducto radicular

Resistencia adhesiva de postes de fibra a los diferentes tercios del conducto radicular

Adhesive resistance of fiber posts to different thirds of the root canal

García Cuerva, M.

Trigo Humaran, M. M.

Tartacovsky, H. J.

Boaventura Dubovik, M. A.

Shin, L. N.

Bertoldi Hepburn, A.

Resumen: En los últimos años resulta de elección la utilización de postes de fibra en la rehabilitación de piezas endodónticamente tratadas. La adhesión entre poste, agente cementante y dentina radicular permitiría lograr una retención de la estructura dentro de las paredes del conducto. El objetivo de este estudio fue comparar la resistencia adhesiva en los tercios cervical, medio y apical, entre la dentina del conducto radicular y el cemento adhesivo utilizado en la cementación de postes de fibra. Se utilizaron 30 premolares inferiores uniradiculares humanos, recientemente extraídos, se realizaron los tratamientos endodónticos, se desobturaron y realizaron las preparaciones con la fresa conformadora número 3 para la cementación de postes White Post DC especial número 3 con cemento Paracore utilizando el protocolo adhesivo del mismo sistema. Las muestras fueron incluidas en acrílico cristal, cortadas en forma perpendicular al eje mayor de la pieza con una máquina de corte y por último se procedió a medir los valores de adhesión de los postes a la superficie interna de los conductos en los tres tercios, con la prueba de Push-out mediante una máquina de ensayo universal. Los resultados arrojaron que las resistencias (media ± DE, MPa) en los tercios cervical, medio y apical fueron 8,74 ± 3,12, 9,38 ± 2,29 y 11,11 ± 2,95, respectivamente. En el tercio apical se registró mayor resistencia. Considerando las limitaciones de esta investigación, se puede concluir que la cementación de postes de fibra con cementos resinosos, presenta mayores valores en el tercio apical y menores en el tercio cervical del conducto radicular con técnica de Push-out.

Abstract: In recent years, the use of fiber posts in rehabilitation of endodontically treated teeth has been the most selected. The adhesion between post, cementing agent and root dentin would allow to achieve a retention of the structure within the canal walls. The aim of this study was to compare the adhesive strength in the cervical, middle and apical thirds, between the dentin of the root canal and the adhesive cement used in the cementation of fiber posts. There were selected 30 recently extracted human uniradicular lower premolars, endodontic treatments were performed. The filling material was removed first and then, they were prepared with the shaping grill number 3 and the cementation of the White Post DC special posts number 3 with Paracore cement was performed using the protocol adhesive. The samples were included in crystal acrylic and then cut perpendicular to the major axis of the piece with a cutting machine and finally the adhesion values of the posts to the internal surface of the conduct were measured in three thirds, with the push-out test using a universal testing machine. The results showed that the resistances (mean ± SD, MPa) in the cervical, middle and apical thirds were 8.74 ± 3.12, 9.38 ± 2.29 and 11.11 ± 2.95, respectively. In the apical third find the highest resistance. Considering the limitations of this research, it can be concluded that in the cementation of fiber posts with resin cements, they have higher values in the apical third and lower values in the cervical third of the root canal with the push out technique.

Fil: García Cuerva, M. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Trigo Humaran, M. M. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Tartacovsky, H. J. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Boaventura Dubovik, M. A. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Shin, L. N. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Bertoldi Hepburn, A. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Endodoncia. Buenos Aires, Argentina.

Rev Fac Odontol, Univ Buenos Aires. 2021; 36(82): 35-42.

p-ISSN 0326-632X

e-ISSN 1668-8538

Universidad de Buenos Aires. Facultad de Odontología.

2021

8 pp.