Interfaz adhesiva entre superficie dentinaria y composites de distintas viscosidades

Interfaz adhesiva entre superficie dentinaria y composites de distintas viscosidades

Adhesive interface between dentin surface and composites of different viscosities

Picca, M.

Lei, M. A.

Toledo, C. N.

Lombardo, N.

Resumen: El objetivo de este estudio fue evaluar la adaptación de las restauraciones de composites de alta y baja viscosidad al sustrato dentinario. Materiales y Métodos: Se utilizaron terceros molares sanos (n=10) y se conservaron en agua destilada a 37°C y se realizaron preparaciones cavitarias calibradas. Los dientes fueron agrupados aleatoriamente en dos grupos (n=5). Los sustratos dentarios de ambos grupos fueron tratados con la técnica de grabado selectivo en esmalte con el ácido fosfórico Ultraetch (Ultradent) y sistema adhesivo universal One Coat 7 Universal (Coltene) según instrucciones del fabricante. En las muestras del grupo 1 se fotopolimerizó, luego se aplicó una capa de 1 mm de resina Flow Brilliant (Coltene) y finalmente se colocó en monobloque resina Everglow (Coltene). Las muestras del grupo 2 se sometieron al mismo tratamiento excepto la capa de composite fluido. Las muestras se seccionaron con cortadora de disco diamantado. Los cortes de 1 mm de espesor fueron analizados con lupa microscópica. Se registraron 4 mediciones de cada muestra de la frecuencia de discontinuidad entre el material y sustrato dentinario. Los resultados se analizaron estadísticamente mediante Prueba de Mann-Whitney a dos colas. Resultados: Los valores de media aritmética (desvío estándar) de cada grupo fueron: Grupo 1: 1,2 (0,80), Grupo 2: 2,4 (0,5). El análisis con la Prueba de Mann-Whitney a dos colas mostró diferencia significativa para el factor material (p<0,05). Conclusión: En las condiciones experimentales de este trabajo puede inferirse que el uso de composite fluido en las restauraciones directas mejoraría la adaptación de la interfaz restauración-estructura dentaria.

Abstract: The objective of this study was to evaluate the adaptation of high and low viscosity composite restorations to the dentin substrate. Materials and methods: Healthy third molars (n=10) were used and preserved in distilled water at 37ºC. A calibrated cavity was made. The teeth were randomly grouped into two groups (n= 5). The dentin substrate of both groups were treated with the selective etching technique with Ultraetch phosphoric acid (Ultradent) on enamel and One Coat 7 Universal adhesive system (Coltene) according to the manufacturer’s instructions. In samples of group 1, it was photopolymerized, then a 1mm layer of Brilliant Flow resin (Coltene) was applied and finally it was placed in a monoblock of Everglow resin (Coltene). The samples of the other group were received the same treatment except for the flowable composite layer. The samples were sectioned. The 1 mm thick sections were analyzed with a microscopic magnifying glass. Four measurements of the frequency of discontinuity between the material and dentinal substrate were recorded for each sample. The results were statistically analyzed using the two-tailed Mann-Whitney test. Results: The mean and standard deviation values of each group were: Group 1: 1.2 (0.80), Group 2: 2.4 (0.5). The analysis with the two-tailed Mann-Whitney test showed a significant difference for the material factor (p<0.05). Conclusion: Under the experimental conditions of this work, it can be concluded that the use of flowable composite in direct restorations would improve the adaptation of the restoration-tooth structure interface.

Fil: Picca, M. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Materiales Dentales. Buenos Aires, Argentina.

Fil: Lei, M. A. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Materiales Dentales. Buenos Aires, Argentina.

Fil: Toledo, C. N. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Materiales Dentales. Buenos Aires, Argentina. / Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Preclínica de Odontología Restauradora. Buenos Aires, Argentina.

Fil: Lombardo, N. Universidad de Buenos Aires. Facultad de Odontología. Cátedra de Preclínica de Odontología Restauradora. Buenos Aires, Argentina.

Rev Fac Odontol, Univ Buenos Aires. 2024; 39(92), 69–75.

ISSN 1668-8538

Universidad de Buenos Aires. Facultad de Odontología.

2024

7 pp.